Effect of heat treatment on wear behaviour of rolled carbon steel in DOT4 brake fluid
- Ajibola, Olawale O., Akinribide, Ojo J., Akinwamide, Samuel O., Olubambi, Peter A.
- Authors: Ajibola, Olawale O. , Akinribide, Ojo J. , Akinwamide, Samuel O. , Olubambi, Peter A.
- Date: 2019
- Language: English
- Type: Article
- Identifier: http://hdl.handle.net/10210/403861 , uj:33859 , Citation: Olawale O Ajibola et al 2019 IOP Conf. Ser.: Mater. Sci. Eng. 628 012014
- Description: Abstract: The wear of heat-treated rolled carbon steels (HTRCSs) were performed under dry and wet sliding in DOT4 brake fluid is successfully investigated and reported in the study. The HTRCSs samples were obtained by heating to and soaking the as-rolled carbon steel (ARCS) at 950 oC prior to quenching or cooling in different media at different selected temperatures between (20 and 250 oC) and atmospheric conditions. The microstructures and wear track patterns of specimens were evaluated using SEM and high-resolution metallurgical microscope. The sliding wear behaviour and wear track patterns of the specimens impressed under 10N normal loads and reciprocating mode was used to assess the wear damages. The obtained wear properties were compared in air and DOT4 fluid environments using Anton Paar TRB tribometer. The results obtained showed that enhanced wear behaviours were obtained from the oil and water quenched samples as compared with the air and furnace cooled samples. The HTRCSs samples are more tolerable than as-rolled sample (ARCS) under dry sliding. However, beside the influences of the heat treatments, the lubricating effect of DOT4 is more pronounced in the results. The CoF ranges from 0.105 to 0.137 for wet sliding while higher CoF values (0.378-0.934) were obtained in the dry sliding.
- Full Text:
- Authors: Ajibola, Olawale O. , Akinribide, Ojo J. , Akinwamide, Samuel O. , Olubambi, Peter A.
- Date: 2019
- Language: English
- Type: Article
- Identifier: http://hdl.handle.net/10210/403861 , uj:33859 , Citation: Olawale O Ajibola et al 2019 IOP Conf. Ser.: Mater. Sci. Eng. 628 012014
- Description: Abstract: The wear of heat-treated rolled carbon steels (HTRCSs) were performed under dry and wet sliding in DOT4 brake fluid is successfully investigated and reported in the study. The HTRCSs samples were obtained by heating to and soaking the as-rolled carbon steel (ARCS) at 950 oC prior to quenching or cooling in different media at different selected temperatures between (20 and 250 oC) and atmospheric conditions. The microstructures and wear track patterns of specimens were evaluated using SEM and high-resolution metallurgical microscope. The sliding wear behaviour and wear track patterns of the specimens impressed under 10N normal loads and reciprocating mode was used to assess the wear damages. The obtained wear properties were compared in air and DOT4 fluid environments using Anton Paar TRB tribometer. The results obtained showed that enhanced wear behaviours were obtained from the oil and water quenched samples as compared with the air and furnace cooled samples. The HTRCSs samples are more tolerable than as-rolled sample (ARCS) under dry sliding. However, beside the influences of the heat treatments, the lubricating effect of DOT4 is more pronounced in the results. The CoF ranges from 0.105 to 0.137 for wet sliding while higher CoF values (0.378-0.934) were obtained in the dry sliding.
- Full Text:
Effect of heat treatment on wear behaviour of rolled carbon steel in DOT4 brake fluid
- Ajibola, Olawale. O., Akinribide, Ojo J., Akinwamide, Samuel O., Olubambi, Peter A.
- Authors: Ajibola, Olawale. O. , Akinribide, Ojo J. , Akinwamide, Samuel O. , Olubambi, Peter A.
- Date: 2019
- Language: English
- Type: Conference proceedings
- Identifier: http://hdl.handle.net/10210/405099 , uj:34002 , Citation: Ajibola, O.O. et al. 2019. Effect of heat treatment on wear behaviour of rolled carbon steel in DOT4 brake fluid.
- Description: Abstract: The wear of heat-treated rolled carbon steels (HTRCSs) were performed under dry and wet sliding in DOT4 brake fluid is successfully investigated and reported in the study. The HTRCSs samples were obtained by heating to and soaking the as-rolled carbon steel (ARCS) at 950 oC prior to quenching or cooling in different media at different selected temperatures between (20 and 250 oC) and atmospheric conditions. The microstructures and wear track patterns of specimens were evaluated using SEM and high-resolution metallurgical microscope. The sliding wear behaviour and wear track patterns of the specimens impressed under 10N normal loads and reciprocating mode was used to assess the wear damages. The obtained wear properties were compared in air and DOT4 fluid environments using Anton Paar TRB tribometer. The results obtained showed that enhanced wear behaviours were obtained from the oil and water quenched samples as compared with the air and furnace cooled samples. The HTRCSs samples are more tolerable than as-rolled sample (ARCS) under dry sliding. However, beside the influences of the heat treatments, the lubricating effect of DOT4 is more pronounced in the results. The CoF ranges from 0.105 to 0.137 for wet sliding while higher CoF values (0.378-0.934) were obtained in the dry sliding.
- Full Text:
- Authors: Ajibola, Olawale. O. , Akinribide, Ojo J. , Akinwamide, Samuel O. , Olubambi, Peter A.
- Date: 2019
- Language: English
- Type: Conference proceedings
- Identifier: http://hdl.handle.net/10210/405099 , uj:34002 , Citation: Ajibola, O.O. et al. 2019. Effect of heat treatment on wear behaviour of rolled carbon steel in DOT4 brake fluid.
- Description: Abstract: The wear of heat-treated rolled carbon steels (HTRCSs) were performed under dry and wet sliding in DOT4 brake fluid is successfully investigated and reported in the study. The HTRCSs samples were obtained by heating to and soaking the as-rolled carbon steel (ARCS) at 950 oC prior to quenching or cooling in different media at different selected temperatures between (20 and 250 oC) and atmospheric conditions. The microstructures and wear track patterns of specimens were evaluated using SEM and high-resolution metallurgical microscope. The sliding wear behaviour and wear track patterns of the specimens impressed under 10N normal loads and reciprocating mode was used to assess the wear damages. The obtained wear properties were compared in air and DOT4 fluid environments using Anton Paar TRB tribometer. The results obtained showed that enhanced wear behaviours were obtained from the oil and water quenched samples as compared with the air and furnace cooled samples. The HTRCSs samples are more tolerable than as-rolled sample (ARCS) under dry sliding. However, beside the influences of the heat treatments, the lubricating effect of DOT4 is more pronounced in the results. The CoF ranges from 0.105 to 0.137 for wet sliding while higher CoF values (0.378-0.934) were obtained in the dry sliding.
- Full Text:
Wear behaviour of cast aluminium silicon (Al-Si) alloy in Dot 4 brake fluid
- Ajibola, Olawale O., Aribo, Sunday, Ige, Oladeji O., Akinribide, Ojo J., Akinwamide, Samuel O., Olubambi, Peter A.
- Authors: Ajibola, Olawale O. , Aribo, Sunday , Ige, Oladeji O. , Akinribide, Ojo J. , Akinwamide, Samuel O. , Olubambi, Peter A.
- Date: 2019
- Language: English
- Type: Conference proceedings
- Identifier: http://hdl.handle.net/10210/403851 , uj:33858 , Citation: Olawale O Ajibola et al 2019 IOP Conf. Ser.: Mater. Sci. Eng. 628 012012
- Description: Abstract: The frictional sliding behaviour of cast Al-Si alloy was investigated with and without DOT 4 hydraulic brake fluid lubrication/environments. Cast Al-Si specimen was produced from wrought alloy and the specimen surface was metallurgically prepared. The ascast product was characterized with aid of micro-hardness tester, the chemical composition was analysed by X-ray fluorescence (XRF), while X-ray diffraction (XRD) was used to identify phases present, microstructures and surface examinations were done on a high resolution metallurgical Optical Microscope. The properties of the polished and worn sample surfaces were examined by Scanning electron microscope (SEM) equipped with Energy dispersive Xray (EDS) facilities. A 6mm diameter alumina ball under varying normal loads (3-10 N) was rubbed against the surface of the cast Al-Si coupon specimen. The dry and wet sliding wear behaviour was assessed based on the CoF-sliding time behaviour. From the results, the average CoF values of 0.9064 for dry and 0.2038 for wet contacts were obtained. Comparatively, 1.03E-06 and 4.21E-07 minimum wear intensities; and 467290 and 132170 wear resistances were obtained for dry and wet contacts respectively. Behaviour of cast Al-Si in DOT4 were compared with its performance in DOT3 regarding the hydraulic brake system application.
- Full Text:
- Authors: Ajibola, Olawale O. , Aribo, Sunday , Ige, Oladeji O. , Akinribide, Ojo J. , Akinwamide, Samuel O. , Olubambi, Peter A.
- Date: 2019
- Language: English
- Type: Conference proceedings
- Identifier: http://hdl.handle.net/10210/403851 , uj:33858 , Citation: Olawale O Ajibola et al 2019 IOP Conf. Ser.: Mater. Sci. Eng. 628 012012
- Description: Abstract: The frictional sliding behaviour of cast Al-Si alloy was investigated with and without DOT 4 hydraulic brake fluid lubrication/environments. Cast Al-Si specimen was produced from wrought alloy and the specimen surface was metallurgically prepared. The ascast product was characterized with aid of micro-hardness tester, the chemical composition was analysed by X-ray fluorescence (XRF), while X-ray diffraction (XRD) was used to identify phases present, microstructures and surface examinations were done on a high resolution metallurgical Optical Microscope. The properties of the polished and worn sample surfaces were examined by Scanning electron microscope (SEM) equipped with Energy dispersive Xray (EDS) facilities. A 6mm diameter alumina ball under varying normal loads (3-10 N) was rubbed against the surface of the cast Al-Si coupon specimen. The dry and wet sliding wear behaviour was assessed based on the CoF-sliding time behaviour. From the results, the average CoF values of 0.9064 for dry and 0.2038 for wet contacts were obtained. Comparatively, 1.03E-06 and 4.21E-07 minimum wear intensities; and 467290 and 132170 wear resistances were obtained for dry and wet contacts respectively. Behaviour of cast Al-Si in DOT4 were compared with its performance in DOT3 regarding the hydraulic brake system application.
- Full Text:
- «
- ‹