Exploration of microstructure and wear behaviours of laser metal deposited Ti6Al4V/Cu composites
- Authors: Erinosho, Mutiu F. , Akinlabi, Esther Titilayo , Pityana, Sisa
- Date: 2016
- Subjects: Dry sliding wear , Laser metal deposition , Microstructures
- Language: English
- Type: Article
- Identifier: http://hdl.handle.net/10210/215408 , uj:21415 , Citation: Erinosho, M.F., Akinlabi, E.T & Pityana, S. 2016. Exploration of microstructure and wear behaviours of laser metal deposited Ti6Al4V/Cu composites.
- Description: Abstract: This paper reports on the investigations conducted on the evolving microstructures and the dry sliding wear of the laser deposited Ti6Al4V/Cu composites. Some selected process parameters were used for the experiments. The laser powers were chosen between 1300 W and 1600 W; scanning speeds were selected between 0.30 m/min and 0.72 m/min while other parameters are as specified in the experimental matrix. It was found that all the composites produced showed good and high-quality microstructures and they exhibited very low or no fusion zones which were as a result of the selected process parameters used. The α-phase region of the composites was found to be harder than the β-phase region. During the composites cooling, the β-phase field transformed to the basal planes of the hexagonal α-phase thereby creating a lower diffusion coefficient of the α-phase as compared to the β-phase counterpart. The Ti6Al4V/Cu composite produced at a laser power of 1397 W and a scanning speed of 0.3 m/min was found to show the lowest percentage of wear volume and coefficient of friction; and happened due to the martensitic structure formed during cooling. Results obtained showed that the poor abrasive wear of titanium alloy has been improved with the addition of copper into their lattices.
- Full Text:
Laser surface modification of Ti6Al4V-Cu for improved microhardness and wear resistance properties
- Authors: Erinosho, Mutiu F , Akinlabi, Esther Titilayo , Pityana, Sisa , Owolabi, Gbadebo
- Date: 2017
- Subjects: Dry sliding wear , Laser metal deposition , Microstructure
- Language: English
- Type: Articles
- Identifier: http://hdl.handle.net/10210/241797 , uj:24925 , Citation: Erinosho, M.F. et al. 2017. Laser surface modification of Ti6Al4V-Cu for improved microhardness and wear resistance properties.
- Description: Abstract: The light weight of Ti6Al4V as a titanium alloy is been amongst the properties that have been tailed for the aerospace and other industrial applications. To modify the properties of this alloy, Cu has been added to host an antimicrobial effect in the revised alloy for marine application. The LMD process on the Ti6Al4V alloy and Cu was been investigated for surface modification in order to combat the problem of biofouling in the marine industry. The investigations focused on the microstructural observations, micro-hardness measurements and dry sliding wear in the presence of 3 and 5 weight percents of Cu. The microstructure results showed that Widmanstätten microstructures were formed in all the samples and lose their robustness towards the fusion zone as a result of the transition of heat sink towards the substrate. The microhardness values of Ti6Al4V-3Cu and Ti6Al4V-5Cu alloys were greatly improved to 547±16 VHN0.5 and 519±54 VHN0.5 respectively. In addition, the behaviour of wear loss on the surface of the Ti6Al4V-Cu alloys exhibited great improvement as compared with the parent...
- Full Text:
Microstructures and dry sliding wear characteristics of the laser metal deposited Ti6Al4V/Cu composites
- Authors: Erinosho, Mutiu F. , Akinlabi, Esther Titilayo , Pityana, Sisa
- Date: 2015
- Subjects: Dry sliding wear , Laser metal deposition , Microstructures , Titanium composites , Copper composites
- Type: Article
- Identifier: uj:5139 , http://hdl.handle.net/10210/14106
- Description: This paper reports on the investigations conducted on the evolving microstructures and the dry sliding wear of the laser deposited Ti6Al4V/Cu composites. Some selected process parameters were used for the experiments. The laser powers were chosen between 1300 W and 1600 W; scanning speeds were selected between 0.30 m/min and 0.72 m/min while other parameters are as specified in the experimental matrix. It was found that all the composites produced showed good and high-quality microstructures and they exhibited very low or no fusion zones which were as a result of the selected process parameters used. The composite produced at a laser power of 1397 W and a scanning speed of 0.3 m/min was found to show the lowest percentage of wear volume and coefficient of friction; and happened due to the martensitic structure formed during cooling. Results obtained showed that the poor abrasive wear of titanium alloy has been improved with the addition of copper into their lattices.
- Full Text: