- Non-destructive testing of dissimilar friction stir welds
- Creator
- Akinlabi, Esther Titilayo, Levy, Adrian C. S., Akinlabi, Stephen A.
- Subject
- Friction stir welding, Non-destructive testing, Aluminum alloys, Copper
- Date
- 2012
- Type
- Article
- Identifier
- uj:5333
- Identifier
- ISSN 2078-0966
- Identifier
- http://hdl.handle.net/10210/8876
- Description
- friction stir welds between 5754 aluminium alloy and C11000 copper. The Friction stir welds of 5754 aluminium alloy and C11000 copper were produced at different tool rotational speeds and feed rates. The tool rotational speed was varied between 600 and 1200 rpm while the feed rate was varied between 50 and 300 mm/min. The visual inspection and the x-ray radiographic testing techniques were employed to conduct the tests; these tests were conducted on the welds to ascertain the joint integrity before characterization to have an idea of the quality of the welds. No visual defects were observed on all the welds considered but the x-ray radiography technique revealed the presence of wormhole defects and discontinuities in some of the welds. It was found that the welds produced at 950 rpm with varied feed rates were the best quality welds produced and this was substantiated with the microstructural evaluation of the joint interface. It was found that these welds have good mixing and metallurgical bonding at the interfaces.
- Publisher
- Proceedings of the World Congress on Engineering
- Rights
- © 2012, authors
- Full Text
- Hits: 2967
- Visitors: 2846
- Downloads: 313
Collections
Conference proceedings
| Thumbnail | File | Description | Size | Format | |||
|---|---|---|---|---|---|---|---|
| View Details Download | CONTENT1 | PDF Document | 778 KB | Adobe Acrobat PDF | View Details Download | ||
| View Details Download | MODS | MODS Metadata | 3 KB | XML Document | View Details Download |