Abstract
Abstract : Spark plasma sintering technique was used to consolidate solid solution of graphite–Ti (C0.9, N0.1) using ultrafine size of graphite and titanium carbonitride powder with carbon to nitrogen composition of 90:10 at 2000 oC for 5 mins. The densification of the sintered graphite (0-1 wt. %) –Ti (C0.9, N0.1) was 98-99% at 2000 oC in the matrix. The carbide rich and Ti rich were the two distinct solid solution phases observed, although Graphite –Ti (C0.9, N0.1) solid solution as a solitary phase was attained at 2000 oC. This could be attributed to changes in the parameters with in the lattice site due to excess heat and causing the solid solutions phases to favour the carbide and titanium phases, respectively. The graphite–Ti (C0.9, N0.1) solid solution upon the application of different load the value of the hardness decreases as the load increases for unreinforced and reinforced Ti (C0.9, N0.1). Furthermore, the fracture toughness (KIC ) was within the range of (1.04 – 7.99) in MPa m1/2.